GK-5E型密炼机混炼工艺的研究

采用具有转子密封圈油密封系统的GK-5E型密炼机，研究不同填料体系胶料在混炼过程中的质量变化、密度及拉伸性能。结果表明：用于密封的机械油会在混炼过程中部分进入到混炼胶中；混炼温度和混炼时间对硫化胶的拉伸性能影响不大；胶料配方中白炭黑用量过大会影响混炼时间，进而对硫化胶的拉伸性能产生影响。     

钛基Ce掺杂SnO_2-RuO_2电极的制备及其对焦化废水的电解处理

采用溶胶-凝胶法制备了经稀土元素Ce掺杂改性的Ti/RuO_2-SnO_2-Ce电极,利用SEM、XRD、EDS等分析方法对电极表面的形貌、物相和涂层成分进行了表征,利用CV曲线、LSV曲线等检测手段对电极的电化学性能进行了测试。以Ti/RuO_2-SnO_2-Ce电极为阳极,钛板为阴极,构建电化学氧化反应装置,并采用其对焦化废水进行电解处理。结果表明,Ti/RuO_2-SnO_2电极经稀土Ce改性后极板表面活性位点数量明显增大,金属涂层的结晶化程度明显增强,电极的催化氧化活性显著提高。室温条件下,保持pH值为7.83,在电流密度为30mA/cm~2,电解时间为30min时,焦化废水经电解处理后COD去除率可达91.63%,TOC去除率可达66.22%,UV254值下降到0.921。     

Research on hydrophobicity of electrospun Fe3O4/PVDF nanofiber membranes under different preparation conditions

Abstract

Preparation condition can affect the structure and the properties of nanofiber membrane. In order to explore suitable conditions to prepare the Fe₃O₄/PVDF nanofiber membrane with good hydrophobicity, the hydrophobicity of Fe₃O₄/PVDF nanofiber membranes obtained by electrospinning was investigated by changing preparation conditions like weight percentage of Fe₃O₄ nanoparticles, blending quality concentration of poly (vinylidene fluoride) (PVDF) and Fe₃O₄ nanoparticles, and positive voltage. And the variations of hydrophobicity of Fe₃O₄/PVDF nanofiber membranes modified by 1H, 1H, 2H, 2H-perfluorodecyl trimethoxysilane were studied. The results show that the hydrophobicity of Fe₃O₄/PVDF nanofiber membranes has changed under different preparation conditions. The contact angles of samples increased after a modification by 1H, 1H, 2H, 2H-perfluorodecyl trimethoxysilane, which indicates that the hydrophobicity of Fe₃O₄/PVDF nanofiber membranes has been enhanced.     

轧制速度对AZ31镁合金管材冷轧成形的影响

轧制速度是三辊式冷轧成形过程中关键的工艺参数，决定其力学特征及温升情况。基于此，本文以冷轧AZ31镁合金管材为研究对象，通过全流程数值仿真计算，对比分析不同轧制速度在各特征变形段对等效应力、等效塑性应变及节点温度的影响规律。结果表明，等效应力、等效塑性应变及节点温度均随轧制速度的增大而增大。通过元胞自动机模型及实验等手段，探明了晶粒在轧制过程中产生连续再结晶并细化的初步组织演变规律；对比分析实验与模拟结果并结合多方面因素，得到800mm/s的轧制速度可以更好的满足工艺要求的结果，为冷轧镁合金管材轧制速度的选择提供依据。     

Novel thermal-sensitive properties of NBT-BZT composite ceramics for high-temperature NTC thermistors

We found for the first time that (1 − x) Na_0.5Bi_0.5TiO₃-xBiZn_0.5Ti_0.5O₃ (NBT–BZT) composite ceramics showed negative temperature coefficient (NTC) at a high temperature. The NBT–BZT nanopowders were successfully prepared by Pechini method. Their ceramics were sintered at 1100°C. The NBT–BZT ceramic exhibited a good linear relationship between logarithm of electrical resistivity (Inρ) and reciprocal of absolute temperature (1000/T) at 250°C–1050°C. The obtained ρ₆₀₀, ρ₉₀₀, and B_600/900 constants of the NBT–ZBT NTC thermistors are approximately 5.92 × 10⁶ to 3.01 × 10⁴ Ω cm, 7.03 × 10³ to 7.60 × 10² Ω cm and 2.3 × 10⁴-1.3 × 10⁴ K, respectively. The electrical characteristics can be tuned to the desired value by changing the Na_0.5Bi_0.5TiO₃ content in the compound. The electrical conductivity in these compounds is due to the electron jumps between Ti³⁺ and Ti⁴⁺ and oxygen-ion conductivity. Results demonstrate a tremendous potential of the studied system for perovskite materials with NTC performance.     

某低品位铜铅锌多金属硫化矿选矿工艺研究

某低品位铜铅锌多金属硫化矿的原矿品位分别为Cu 0.47%、Pb 1.236%和Zn 0.891%。矿石中铜铅锌有用矿物的嵌布粒度较细且共生关系较复杂。试验着重探讨了磨矿细度、浮选捕收剂和调整剂的优化,在解决矿物有效解离的前提下,提高铜铅锌浮选分离的选择性。当原矿磨矿细度为-0.074mm占80%时,采用乙硫氮作捕收剂,石灰、硫酸锌和亚硫酸钠作调整剂,粗选获得的铜铅混合粗精矿再磨至-0.043mm占81.31%后,经两次精选获得铜铅混合精矿。铜铅混合精矿采用活性炭脱药,亚硫酸钠和CMC组合抑铅,Z200浮选铜,实现了铜铅分离。铜铅混合浮选尾矿,采用硫酸铜活化,丁基黄药作捕收剂,浮选获得锌精矿。最终浮选指标为:铜精矿的铜品位27.26%,铜回收率80.62%;铅精矿的铅品位59.35%,铅回收率85.20%;锌精矿的锌品位41.14%,锌回收率为82.74%。为该低品位铜铅锌多金属硫化矿资源的开发利用提供了可行的技术方案。     

X70配套埋弧焊丝用H08D盘条的研制

介绍了北营公司X70配套埋弧焊丝用H08D盘条的开发研制情况.其生产工艺的关键点为:转炉采用“双渣法除磷”,脱氧合金化在转炉和LF炉两个阶段完成,连铸采用结晶器电磁搅拌及末端电磁搅拌、恒定拉速;盘条采用控冷控轧及轧后延迟型斯太尔摩冷却工艺等措施.生产的成品盘条成分、力学性能、金相组织等指标均满足客户拉拔工艺要求.     

冷轧预变形对新型铝锂合金的时效析出与力学性能影响

采用大气熔炼铸造及热变形方法制备了Al-4.5Cu-1Li-0.7Mg-1Zn-0.3Ag-0.3Mn-0.2Zr新型铝锂合金板材。通过维氏硬度、拉伸性能、扫描电镜、透射电镜等方法，研究了固溶后不同冷轧预变形量对显微组织和力学性能影响。结果表明，时效前的冷轧预变形量有效促进了新型铝锂基体合金中T1(Al2CuLi)相的析出与均匀分布，减少了θ′(Al2Cu)相的体积分数。冷轧预变形量的增加，缩短了峰时效时间，晶界析出相由连续析出变为非连续析出，无沉淀析出区宽度变小。当冷轧预变形量为15%时，时效态合金的屈服强度与抗拉强度分别达到了668 MPa、690 MPa，延伸率保持在7.9%。     

超疏水表面在金属防护中应用的研究进展

超疏水表面由于具有独特的微纳米粗糙结构和低表面能性质,能形成空气垫物理屏障层,减小材料表面与水或其他腐蚀介质之间的接触面积,因此被广泛应用于金属的腐蚀防护。首先简单介绍了超疏水表面的相关理论,主要包括Young氏方程、Wenzel模型和Cassie-Baxter模型。然后,归纳总结了三种制备超疏水表面的有效途径:在低表面能物质上构建微纳米级粗糙结构;先构建出具有微纳米级的粗糙结构,再对表面进行低表面能修饰;一步法完成低表面能修饰和微纳米级粗糙结构的构建。在此基础上,详细地综述了常见的超疏水表面(薄膜或涂层)在金属防护中的应用。进一步介绍了通过在超疏水体系中引入缓蚀剂的方式,构建具有主动防护功能的超疏水表面,并介绍了此种超疏水表面在金属防护中的应用。最后指出了目前的超疏水表面在制备工艺以及耐久性等方面存在的问题,并对其在金属防护领域的应用前景和发展方向作出了展望。